COPPER : MECHANICAL CHARACTERISTICS

Designation Size mm
Hardness
Tensile
strengthRm
Yield point
0,2 % Rp 0,2
Elongation
Round,
square
hexagonal
Flat
A100 mm
A
  Material  
Thickness
Widht
HB
HV
N/mm2
N/mm2
%
%
Symbol Number
Hardness
from
over
of
up to and including
from
over
of
up to and including
from
over
of
 up to and including
min.
max.
min.
max.
min.
  
min.
min.
   
D
2
-
80
0,5
-
40
1
-
200
  
Drawn product
without any mecchaniccal characteristics.
H035*
2
-
80
0,5
-
40
1
-
200
35
65
35
65
-
-
-
-
Cu-ETP CW004A
R200*
2
-
80
1
-
40
5
-
200
-
-
-
-
200
max.120
25
35
Cu-FRHC CW005A                                    
Cu-OF CW008A
H065
2
-
80
0,5
-
40
1
-
200
65
90
70
95
-
-
-
-
CuAg 0,04 CW011A
R250
2
-
10
1
-
10
5
-
200
-
-
-
-
250
min.200
8
12
CuAg 0,07 CW012A
R250
-
10
30
-
-
-
-
-
-
-
-
-
-
250
min.180
-
15
CuAg 0,10 CW013A
R230
-
30
80
-
10
40
-
10
200
-
-
-
-
230
min.160
-
18
CuAg 0,04P CW014A                                    
CuAg 0,07P CW015A
H085
2
-
40
0,5
-
20
1
-
120
85
110
90.
115
-
-
-
-
CuAg 0,10P CW016A
H075
-
40
80
 -
20
40
-
20
160
75
100
80
105
-
-
-
-
CuAg 0,04(OF) CW017A
R300
2
-
20
1
-
10
5
-
120
-
-
-
-
300
min.260
5
8
CuAg 0,07(OF) CW018A
R280
-
20
40
-
10
20
-
10
120
-
-
-
-
280
min.240
-
10
CuAg 0,10(OF) CW019A
R260
-
40
80
-
20
40
-
20
160
-’
-
-
-
260
min.220
-
12
Cu-PHC CW020A                                    
Cu-HCP CW021A
H100
2
-
10
0,5
-
5
1
-
120
100
-
110
-
-
-
-
-
   
R350
2
-
10
1
-
5
5
-
120
-
-
-
-
350
min.320
3
5
NOTE : 1 N/mm2 is equivalent in 1 MPa.      -     * Annealing